Título: Characterization of WO3 Nanostructures used in the degradation of Methylparaben
Autor: García Antón, José; Cifre Herrando, Mireia; Roselló Márquez, Gemma; García García, Dionisio Miguel
Resumen: The data were use to study the degradation of Methylparaben using WO3 Nanostructures. WO3 nanostructures were synthesized with different complexing agents (0.05 M H2O2 and 0.1 M citric acid) and annealing conditions (400 _C, 500 _C and 600 _C) to obtain optimal WO3 nanostructures to use them as a photoanode in the photoelectrochemical (PEC) degradation of an endocrine disruptor chemical. X-ray photoelectron spectroscopy was performed to provide information of the electronic states of the nanostructures. The crystallinity of the samples was observed by a confocal Raman laser microscope and X-ray diffraction. Furthermore, photoelectrochemical measurements (photostability, photoelectrochemical impedance spectroscopy, Mott–Schottky and water-splitting test) were also performed using a solar simulator with AM 1.5 conditions at 100 mW_cm-2. Once the optimal nanostructure was obtained, the PEC degradation of methylparaben was carried out. It was followed by ultra-high-performance liquid chromatography and mass spectrometry, which allowed to obtain the concentration of the contaminant during degradation and the identification of degradation intermediates.
Descripción: Estos datos han sido empleados en el artículo ya publicado (OPEN ACCES): Nanomaterials 12 (2022) 4286, https://doi.org/10.3390/nano12234286